Umrechnungstabelle
Fläche A
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
cm2 | 0,155 | square inch |
square inch | 6,45 | cm2 |
Kraft F
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
kp | 9,81 | N = kg m/s2 |
N = kg m/s2 | 0,102 | kp |
Länge L
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
cm | 0,3937 | inch |
inch | 2,54 | cm |
Magnetische Feldstärke H
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
Ampere-turns/inch | 39,37 | A/m |
A/cm | 100 | A/m |
A/m | 0,01257 | Oe |
A/m | 0,01 | A/cm |
A/m | 0,0254 | Ampere-turns/inch |
Oe | 79,6 | A/m |
Magnetische Flussdichte B bzw. Magnetische Polarisation J
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
G | 10-4 | T |
lines/square inch | 1,55 * 10-5 | T |
T = Wb/m2 = Vs/m2 | 10-4 | Wb/cm2 = Vs/cm2 |
T | 104 | G |
T | 6,45 * 104 | lines/square inch |
Vs/cm2 | 104 | T |
Masse m
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
g | 0,0353 | ounce |
kg | 2,205 | pound |
ounce | 28,35 | g |
pound | 0,4536 | kg |
Ummagnetisierungsverlust Ps
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
W/kg | 0,4536 | W/lb |
W/lb | 2,205 | W/kg |
Temperatur T
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
°C | x 1,8 + 32 | °F |
°F | x 0,556 - 17,8 | °C |
Festigkeit Re, Rp, Rm
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
kp/mm2 | 9,81 | N/mm2 |
N/mm2 | 0,102 | kp/mm2 |
N/mm2 | 145 | pounds/square inch (psi) |
psi | 6,90 * 10-3 | N/mm2 |
Volumen V
IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
---|---|---|
cm3 | 0,061 | cubic inch |
cubic inch | 16,4 | cm3 |